Wholesale Uv Stable Polyurethane Resin Suppliers – Polyether polyurethane acrylate for plastic coatings – Zicai
Wholesale Uv Stable Polyurethane Resin Suppliers – Polyether polyurethane acrylate for plastic coatings – Zicai Detail:
Product Detail
| Product code | ZC6202 |
| Appearance | Colorless or yellowish transparent liquid |
| Viscosity | 7000 -20000 at 25 Celsius Degree |
| Functional | 2 |
| Product features | Flexibility and good adhesion |
| Application | Paper, plastic coating, wood adhesion primer |
| Specification | 20KG 25KG 200KG |
| Acid value (mgKOH/g) | <0.5 |
| Transport Package | Barrel |
Product Description
Product Code: ZC6202
Product ZC6202 is a brand product of the company. Its chemical name is polyether polyurethane acrylate. It is a colorless or yellowish transparent liquid with good flexibility and adhesion. It is mainly used for paper, plastic coating and wood adhesion primer. Aromatic polyurethane acrylate
Add polyether (polyester) diol and polymerization inhibitor into a four port flask equipped with stirring machine, thermometer and condenser tube, stir evenly, then add TDI, raise the temperature to 70-80 ℃ for reaction for 1.5 hours, detect the NCO value, then add hydroxyethyl acrylate (hydroxypropyl acrylate), add catalyst, continue the reaction for 3 hours, and detect that the NCO value is equal to 0. The viscosity of aromatic polyurethane acrylate was measured by sampling, and the performance of aromatic polyurethane acrylate was tested by adding 3% – 4% photoinitiato.Please keep cool or dry place, and avoid sun and heat;Storage temperature does not exceed 40 ºC, storage conditions under normal conditions for at least 6 months.
Initiated with polyethylene glycol (PEG, MW 1000) ε- Caprolactone（ ε- The soft segment of polyether ester block copolymer diol (pCEC) was prepared by ring opening, reacted with diisocyanate (toluene diisocyanate or diphenylmethane diisocyanate) and hydroxyethyl methacrylate, and then cured to obtain polyether ester polyurethane acrylate material (PUA) The composition and structure of PUA were characterized The results show that increasing PCL segment can improve the crystallinity of PUA material, but reduce the water absorption and degradation rate The enzymatic hydrolysis rate of PUA was higher than that of PUA Pcec2000-tdi material has excellent hydrophilicity and degradation performance. The water absorption is as high as 65.24% in 72 hours and can be completely degraded in enzyme solution within 11 weeks This kind of PUA material has the potential to be used in tissue engineering materials.
Product detail pictures:
Related Product Guide:
The business keeps to the operation concept "scientific management, premium quality and efficiency primacy, customer supreme for Wholesale Uv Stable Polyurethane Resin Suppliers – Polyether polyurethane acrylate for plastic coatings – Zicai , The product will supply to all over the world, such as: Wellington, Norwegian, Plymouth, Our solutions have national accreditation requirements for qualified, good quality items, affordable value, was welcomed by individuals all over the world. Our goods will continue to improve inside the order and appear forward to cooperation with you, Really should any of those items be of interest to you, please letus know. We will be satisfied to provide you a quotation up on receipt of the detailed needs.
By Annabelle from Turkmenistan - 2017.12.19 11:10
The company account manager has a wealth of industry knowledge and experience, he could provide appropriate program according our needs and speak English fluently.
By Nicci Hackner from New Zealand - 2018.12.30 10:21