Wholesale Uv Cure Polyester Resin Factory – Polyester acrylate oligomer UV resin – Zicai
Wholesale Uv Cure Polyester Resin Factory – Polyester acrylate oligomer UV resin – Zicai Detail:
Product Detail
| Product code | ZC8605 |
| Appearance | Yellowish transparent liquid |
| Viscosity | 18000 -30000 at 25 Celsius Degree |
| Functional | 2 |
| Product features | Yellowing resistance, good leveling, moderate flexibility, fast curing and good pigment wettability |
| Application | Ink, wood, paper, plastic coating and vacuum electroplating finish, white paint system |
| Specification | 20KG 25KG 200KG |
| Acid value (mgKOH/g) | <5 |
| Transport Package | Barrel |
Product Description
The chemical name of product ZC8605 is polyester acrylate. It is a kind of yellowish transparent liquid. Its customers are mainly used in nail varnish and color glue. Its wettability effect is the best product in the company’s resin system. It has leveling flexibility, good yellowing resistance and fast curing. It is mainly used in ink, wood, paper, plastic coating and vacuum electroplating finish, It can also be used in white paint system.Polyester acrylic resin，Add anhydride, acrylic acid, polymerization inhibitor and catalyst into a four port flask equipped with stirring machine, thermometer and condenser tube, stir evenly, raise the temperature to 110 ℃, react for 5-6 hours, and detect the acid value until the acid value is less than 5. The viscosity of polyester acrylic resin was measured by sampling, and the performance of polyester acrylic resin was tested by adding 3% – 4% photoinitiator.
Polyester acrylic UV resin with excellent properties was synthesized by hydroxyl terminated polyester and acrylic acid under appropriate conditions Water is produced during the reaction of polyester (double ended hydroxyl) with acrylic acid, which determines that the synthesis process is different from that of other UV resins The effects of temperature, azeotropic solvent and catalyst on the properties of polyester resin and polyester acrylic UV resin were discussed The conclusions are as follows: the synthesis of polyester is carried out at 180 ℃, xylene is azeotropic solvent and H3PO4 is catalyst; The synthesis of polyester acrylic UV resin was carried out at 110-120 ℃, toluene as azeotropic solvent and p-toluenesulfonic acid as catalyst The role of polymerization inhibitor in the synthesis of UV resin was discussed
Storage Conditions
Please keep cool or dry place, and avoid sun and heat;Storage temperature does not exceed 40 ºC, storage conditions under normal conditions for at least 6 months.
Use Matters
Avoid touching the skin and clothing, wear protective gloves when handling;
Leak with a cloth when the leak, clean with esters or ketones for details, please refer to the Material Safety Instructions (MSDS);
Each batch of goods to be tested before they can be put into production
Video
Application and Product images
Product detail pictures:
Related Product Guide:
We always stick to the principle "Quality First, Prestige Supreme". We are fully committed to providing our clients with competitively priced quality products, prompt delivery and professional service for Wholesale Uv Cure Polyester Resin Factory – Polyester acrylate oligomer UV resin – Zicai , The product will supply to all over the world, such as: Hanover, Algeria, South Korea, They are sturdy modeling and promoting effectively all over the world. Never ever disappearing major functions within a quick time, it's a have to for you of fantastic good quality. Guided by the principle of Prudence, Efficiency, Union and Innovation. the corporation. ake an excellent efforts to expand its international trade, raise its organization. rofit and raise its export scale. We are confident that we are going to have a bright prospect and to be distributed all over the world in the years to come.
By Evangeline from Angola - 2018.02.08 16:45
The company's products can meet our diverse needs, and the price is cheap, the most important is that the quality is also very nice.
By Amelia from Bangalore - 2017.11.12 12:31