Wholesale Aromatic Polyurethane Acrylate Suppliers – Polyether polyurethane acrylate for plastic coatings – Zicai
Wholesale Aromatic Polyurethane Acrylate Suppliers – Polyether polyurethane acrylate for plastic coatings – Zicai Detail:
Product Detail
| Product code | ZC6202 |
| Appearance | Colorless or yellowish transparent liquid |
| Viscosity | 7000 -20000 at 25 Celsius Degree |
| Functional | 2 |
| Product features | Flexibility and good adhesion |
| Application | Paper, plastic coating, wood adhesion primer |
| Specification | 20KG 25KG 200KG |
| Acid value (mgKOH/g) | <0.5 |
| Transport Package | Barrel |
Product Description
Product Code: ZC6202
Product ZC6202 is a brand product of the company. Its chemical name is polyether polyurethane acrylate. It is a colorless or yellowish transparent liquid with good flexibility and adhesion. It is mainly used for paper, plastic coating and wood adhesion primer. Aromatic polyurethane acrylate
Add polyether (polyester) diol and polymerization inhibitor into a four port flask equipped with stirring machine, thermometer and condenser tube, stir evenly, then add TDI, raise the temperature to 70-80 ℃ for reaction for 1.5 hours, detect the NCO value, then add hydroxyethyl acrylate (hydroxypropyl acrylate), add catalyst, continue the reaction for 3 hours, and detect that the NCO value is equal to 0. The viscosity of aromatic polyurethane acrylate was measured by sampling, and the performance of aromatic polyurethane acrylate was tested by adding 3% – 4% photoinitiato.Please keep cool or dry place, and avoid sun and heat;Storage temperature does not exceed 40 ºC, storage conditions under normal conditions for at least 6 months.
Initiated with polyethylene glycol (PEG, MW 1000) ε- Caprolactone（ ε- The soft segment of polyether ester block copolymer diol (pCEC) was prepared by ring opening, reacted with diisocyanate (toluene diisocyanate or diphenylmethane diisocyanate) and hydroxyethyl methacrylate, and then cured to obtain polyether ester polyurethane acrylate material (PUA) The composition and structure of PUA were characterized The results show that increasing PCL segment can improve the crystallinity of PUA material, but reduce the water absorption and degradation rate The enzymatic hydrolysis rate of PUA was higher than that of PUA Pcec2000-tdi material has excellent hydrophilicity and degradation performance. The water absorption is as high as 65.24% in 72 hours and can be completely degraded in enzyme solution within 11 weeks This kind of PUA material has the potential to be used in tissue engineering materials.
Product detail pictures:
Related Product Guide:
We now have a highly efficient crew to deal with inquiries from clients. Our intention is "100% shopper pleasure by our merchandise quality, price tag & our staff service" and take pleasure in a very good standing amongst purchasers. With quite a few factories, we can easily provide a wide vary of Wholesale Aromatic Polyurethane Acrylate Suppliers – Polyether polyurethane acrylate for plastic coatings – Zicai , The product will supply to all over the world, such as: Colombia, Rwanda, Barbados, Our factory is equipped with complete facility in 10000 square meters, which makes us be able to satisfy the producing and sales for most auto part products. Our advantage is full category, high quality and competitive price! Based on that, our products win a high admiration both at home and abroad.
By Octavia from Malaysia - 2018.11.28 16:25
The company can think what our think, the urgency of urgency to act in the interests of our position, can be said this is a responsible company, we had a happy cooperation!
By Olivia from India - 2018.03.03 13:09