China Acrylic Modified Polyurethane – Polyether polyurethane acrylate for plastic coatings – Zicai
China Acrylic Modified Polyurethane – Polyether polyurethane acrylate for plastic coatings – Zicai Detail:
Product Detail
| Product code | ZC6202 |
| Appearance | Colorless or yellowish transparent liquid |
| Viscosity | 7000 -20000 at 25 Celsius Degree |
| Functional | 2 |
| Product features | Flexibility and good adhesion |
| Application | Paper, plastic coating, wood adhesion primer |
| Specification | 20KG 25KG 200KG |
| Acid value (mgKOH/g) | <0.5 |
| Transport Package | Barrel |
Product Description
Product Code: ZC6202
Product ZC6202 is a brand product of the company. Its chemical name is polyether polyurethane acrylate. It is a colorless or yellowish transparent liquid with good flexibility and adhesion. It is mainly used for paper, plastic coating and wood adhesion primer. Aromatic polyurethane acrylate
Add polyether (polyester) diol and polymerization inhibitor into a four port flask equipped with stirring machine, thermometer and condenser tube, stir evenly, then add TDI, raise the temperature to 70-80 ℃ for reaction for 1.5 hours, detect the NCO value, then add hydroxyethyl acrylate (hydroxypropyl acrylate), add catalyst, continue the reaction for 3 hours, and detect that the NCO value is equal to 0. The viscosity of aromatic polyurethane acrylate was measured by sampling, and the performance of aromatic polyurethane acrylate was tested by adding 3% – 4% photoinitiato.Please keep cool or dry place, and avoid sun and heat;Storage temperature does not exceed 40 ºC, storage conditions under normal conditions for at least 6 months.
Initiated with polyethylene glycol (PEG, MW 1000) ε- Caprolactone（ ε- The soft segment of polyether ester block copolymer diol (pCEC) was prepared by ring opening, reacted with diisocyanate (toluene diisocyanate or diphenylmethane diisocyanate) and hydroxyethyl methacrylate, and then cured to obtain polyether ester polyurethane acrylate material (PUA) The composition and structure of PUA were characterized The results show that increasing PCL segment can improve the crystallinity of PUA material, but reduce the water absorption and degradation rate The enzymatic hydrolysis rate of PUA was higher than that of PUA Pcec2000-tdi material has excellent hydrophilicity and degradation performance. The water absorption is as high as 65.24% in 72 hours and can be completely degraded in enzyme solution within 11 weeks This kind of PUA material has the potential to be used in tissue engineering materials.
Product detail pictures:
Related Product Guide:
So that you can finest fulfill client's demands, all of our operations are strictly performed in line with our motto "High Excellent, Competitive Price, Fast Service" for China Acrylic Modified Polyurethane – Polyether polyurethane acrylate for plastic coatings – Zicai , The product will supply to all over the world, such as: Bogota, Somalia, Costa rica, To have much more enterprise. ompanions, we've got updated the item list and seek for optimistic co-operation. Our web-site shows the latest and complete information and facts about our goods list and company. For further acknowledge, our consultant service group in Bulgaria will reply to all of the inquiries and complications immediately. They're going to make their finest effort to meet buyers need. Also we support the delivery of absolutely free samples. Business visits to our business in Bulgaria and factory are generally welcome for a win-win negotiation. Hope to expertise a happy company co-operation perform with you.
By Ellen from Miami - 2017.09.22 11:32
It is really lucky to meet such a good supplier, this is our most satisfied cooperation, I think we will work again!
By Elaine from Tunisia - 2017.10.27 12:12